3:1 heat shrink combustion-resistant black adhesive tubing
Type: TTK(3:1) black (TU 2247-021-97284872-2006)
- Designed for sealing, insulation, and corrosion protection of contact joints in the electric power and telecommunication industries
- Extended shrinkage ratio: 3:1
- Material: polyolefin, does not support combustion
- Color: Black
- A layer of hot melt glue is applied to the entire inner surface of the shrink tubing by co-extrusion
- Black tubes are resistant to UV radiation
- During shrinkage, the adhesive sublayer melts down, fills all irregularities of the surface, and completely seals the joints
- Delivery package: 1 m cut
- Installation tools: TT-1800 heat gun or portable butane burners (KVT)
|
Elongation at fracture |
not less than 350 % |
|
Shrinkage temperature |
115–140 °C |
|
Operating temperature |
-55 °C to +125 °C |
|
Tensile strength |
not less than 10 MPa |
|
Dielectric strength |
not less than 20 kV/mm |
|
Operating voltage |
up to 1000 V |
|
Volumetric resistivity |
1014 ohm*cm |
Product Description and Features
DESIGN VERSION: NG
GUARANTEE OF LEAKAGE TIGHTNESS
|
commodity items, color |
Optimal shrinkage range (mm) |
delivery package |
adhesive layer |
Dimensions (mm) |
min. quantity for release |
cost unit |
||
|
D (not less than) |
d (not more than) |
T (after shrinkage) |
||||||
|
TTK(3:1)-3/1(KVT) |
2.7-1.2 |
cut: 1m |
hot melt |
3 |
1 |
1.1 |
10 |
m |
|
TTK(3:1)-4.8/1.6(KVT) |
4.3–1.9 |
cut: 1m |
hot melt |
4.8 |
1.6 |
1 |
10 |
m |
|
TTK(3:1)-6/2(KVT) |
5.4–2.4 |
cut: 1m |
hot melt |
6 |
2 |
1.0 |
10 |
m |
|
TTK(3:1)-9/3(KVT) |
8.1–3.6 |
cut: 1m |
hot melt |
9 |
3 |
1.4 |
10 |
m |
|
TTK(3:1)-12/4(KVT) Min. quantity for release: 10 m product code: 59697 |
10.8–4.8 |
cut: 1m |
hot melt |
12 |
4 |
1.6 |
10 |
m |
|
TTK(3:1)-18/6(KVT) |
16.2–7.2 |
cut: 1m |
hot melt |
18 |
6 |
2.1 |
10 |
m |
|
TTK(3:1)-24/8(KVT) |
21.6–9.6 |
cut: 1m |
hot melt |
24 |
8 |
2.4 |
10 |
m |
|
TTK(3:1)-30/10(KVT) |
27.0–12.0 |
cut: 1m |
hot melt |
30 |
10 |
2.4 |
10 |
m |
|
TTK(3:1)-39/13(KVT) |
35.1–15.6 |
cut: 1m |
hot melt |
39 |
13 |
2.4 |
10 |
m |
|
TTK(3:1)-50/17(KVT) |
45.0–20.4 |
cut: 1m |
hot melt |
50 |
17 |
2.4 |
10 |
m |